prikaz prve stranice dokumenta Naknadna oksidacija nitriranih dijelova
  Download
PDF 2.96 MB
undergraduate thesis
Naknadna oksidacija nitriranih dijelova
Zagreb: University of Zagreb, Faculty of Mechanical Engineering and Naval Architecture, 2021. urn:nbn:hr:235:103321
Penava, Stipo
University of Zagreb
Faculty of Mechanical Engineering and Naval Architecture

Cite this document

Penava, S. (2021). Naknadna oksidacija nitriranih dijelova (Undergraduate thesis). Zagreb: University of Zagreb, Faculty of Mechanical Engineering and Naval Architecture. Retrieved from https://urn.nsk.hr/urn:nbn:hr:235:103321

Penava, Stipo. "Naknadna oksidacija nitriranih dijelova." Undergraduate thesis, University of Zagreb, Faculty of Mechanical Engineering and Naval Architecture, 2021. https://urn.nsk.hr/urn:nbn:hr:235:103321

Penava, Stipo. "Naknadna oksidacija nitriranih dijelova." Undergraduate thesis, University of Zagreb, Faculty of Mechanical Engineering and Naval Architecture, 2021. https://urn.nsk.hr/urn:nbn:hr:235:103321

Penava, S. (2021). 'Naknadna oksidacija nitriranih dijelova', Undergraduate thesis, University of Zagreb, Faculty of Mechanical Engineering and Naval Architecture, accessed 24 April 2024, https://urn.nsk.hr/urn:nbn:hr:235:103321

Penava S. Naknadna oksidacija nitriranih dijelova [Undergraduate thesis]. Zagreb: University of Zagreb, Faculty of Mechanical Engineering and Naval Architecture; 2021 [cited 2024 April 24] Available at: https://urn.nsk.hr/urn:nbn:hr:235:103321

S. Penava, "Naknadna oksidacija nitriranih dijelova", Undergraduate thesis, University of Zagreb, Faculty of Mechanical Engineering and Naval Architecture, Zagreb, 2021. Available at: https://urn.nsk.hr/urn:nbn:hr:235:103321

Please login to the repository to save this object to your list.
Metadata
TitleNaknadna oksidacija nitriranih dijelova
Title (english)Post oxidation of nitrided parts
AuthorStipo Penava
MentorBožidar Matijević (mentor)
Committee memberBranko Bauer (predsjednik povjerenstva)
GranterUniversity of Zagreb
Faculty of Mechanical Engineering and Naval Architecture
Zagreb
Defense date and country2021-02-25, Croatia
Scientific / art field,
discipline and subdiscipline		TECHNICAL SCIENCES
Mechanical Engineering
Abstract
Završni rad sastoji se od ispitivanja roto rašpa za obradu drva i mekih materijala. Rad se može podijeliti na teorijski i eksperimentalni dio. Prvi, teorijski dio, sadržava postupke obrade, a u eksperimentalnom dijelu ispitani su uzorci. U ovom radu ispitana su dva uzorka. Obrada ispitanih uzoraka izvršena je metodama nitrokarburiranja u solnoj kupki (TENIFER) te postupak koji se sastoji od naknadne oksidacije QPQ (Quenching Polishing Quenching) nitrokarburiranog sloja. Na oba uzorka provedeno je ispitivanje debljine nitriranog sloja, mikrostrukture i tvrdoće. Na osnovu rezultata provedenih ispitivanja možemo zaključiti kako samim TENIFER postupkom dolazi do veće površinske tvrdoće uzorka, odnosno, veće otpornosti trošenja. No ovaj postupak dovodi do estetski neprihvatljivog izgleda površine. Stoga je proveden QPQ postupak kako bi se dobila bolja kemijska postojanost, stvaranjem oksida Fe3O4, dobiva se magnetit crne boje. Međutim, ovakvim postupkom neizbježno je smanjenje površinske tvrdoće.
Abstract (english)
The final paper consists of testing roto rasp for processing wood and soft materials. The paper can be divided into theoretical and experimental part. The first, theoretical part, contains procedures, and samples were tested in the experimental part. Two samples were tested in this paper. Processing of the tested samples was performed by methods of nitrocarburization in salt bath (TENIFER) and a process consisting of subsequent oxidations of QPQ (Quenching Polishing Quenching) of nitrocarburized layer. Testing of nitrated layer thickness, microstructure and hardness was proven on both samples. The test leads to the conclusion that the TENIFER process itself leads to higher surface hardness of the sample. But this procedure leads to an aesthetically unacceptable surface appearance. Therefore, a QPQ procedure was performed. In order to obtain better chemical resistance, a black magnetite is obtained by producing Fe3O4. However, such a procedure inevitably reduces the surface hardness.
Keywords
Keywords (english)
Languagecroatian
URN:NBNurn:nbn:hr:235:103321
Study programmeTitle: Mechanical Engineering
Study programme type: university
Study level: undergraduate
Academic / professional title: sveučilišni/a prvostupnik/ prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka strojarstva (sveučilišni/a prvostupnik/ prvostupnica (baccalaureus/baccalaurea) inženjer/inženjerka strojarstva)
Type of resourceText
File originBorn digital
Access conditionsOpen access
Terms of useLicence In copyright icon
RepositoryRepository of Faculty of Mechanical Engineering and Naval Architecture University of Zagreb
Created on2021-02-23 11:42:35

(©) Nacionalna i sveučilišna knjižnica u Zagrebu 2015. Sva prava pridržana. | Hrvatske bratske zajednice 4 p.p. 550, 10000 Zagreb, Hrvatska Tel. ++ 385 1 616-4040
OIB: 84838770814 | IBAN: HR66 2340 0091 1000 1008 1, Porezni broj (PDV identifikacijski broj) - VAT Number: HR84838770814
Prijava u repozitorij